铜助剂对费-托合成沉淀铁催化剂的影响

铜助剂对费-托合成沉淀铁催化剂的影响 Effects of Copper on the Precipitated Iron Fischer-Tropsch Catalysts 张煜华 1 2 first-author 熊海峰 1 2 李金林 1 2 中南民族大学化学与生命科学学院催化材料科学湖北省重点实验室 中南民族大学化学与生命科学学院催化材料科学湖北省重点实验室 用X 射线衍射、氢气程序升温还原、氢气程序升温脱附和氧滴定等技术对沉淀法制备的铜 铁费 托合成催化剂进行了表征.结果表明,铜促进了Fe2O3→Fe3O4的还原,且使该过程的起始还原温度明显降低,但对Fe3O4→FeO→Fe两个还原过程无影响;通过浸渍法加入的铜虽可较好地分散在催化剂表面,但却导致了氢气的吸附量减少,同时由于Cu和Fe之间可能存在的相互作用,使催化剂中的还原态物质在氧滴定中不能被充分氧化;Cu还有助于Fe在催化剂表面的分散. The iron Fischer-Tropsch catalysts were prepared by precipitation. The catalysts were characterized by X-ray diffraction （XRD）, hydrogen temperature programmed reduction (H 2 -TPR), hydrogen temperature programmed desorption (H 2 -TPD) and oxygen titration respectively. The results show that copper can facilitate the reduction of iron oxide, especially the transformation of Fe 2 O 3 →Fe 3 O 4 ,however, copper cannot affect the reduction of Fe 3 O 4 →FeO→Fe. Though the copper was dispersed well on the catalyst by impregnation, the metal-metal interaction between iron and copper influences the reoxidation of （iron）-copper catalysts and the hydrogen-chemisorption properties of catalyst. The copper can help the dispersing of iron on the catalyst. 费托合成 铁催化剂 铜助剂 X射线衍射 氢气程序升温还原 氢气程序升温脱附 氧滴定 Fischer-Tropsch synthesis precipitated iron catalyst copper promoted XRD（X-ray diffraction） H2-TPR（hydrogen temperature programmed reduction） H2-TPD（hydrogen temperature programmed desorption） oxygen titration O643.3 国家自然科学基金（20373090）;湖北省杰出青年人才基金（2003ABB013）;教育部留学归国人员科研启动基金;教育部优秀青年教师资助计划项目;国家民委重点基金 2004-06-01 2021-04-01 6